Distinguish between 3003 aluminum plate and 5052 aluminum plate

Edit:admin Date: 2017-03-10 09:11
As we all know, 3003 aluminum plate and 5052 aluminum plate are the most common alloy aluminum, aluminum is the most representative of the two series of two brands. From the chemical composition, 3003 aluminum plate is aluminum-manganese alloy, the main alloying element is manganese. 5052 aluminum plate is aluminum-magnesium alloy, the main alloying element is magnesium. 3003 aluminum content slightly higher than 5052 aluminum.

The tensile strength of 3003H24 aluminum plate is 145-195Rm / MPa, and the tensile strength of 5052H24 aluminum plate is as high as 230-280Rm / MPa, which is much higher than 3003H24 aluminum plate. The extension strength of 3003H24 aluminum plate is 115Rm / While the extension strength of the 5052H24 aluminum plate is 150 Rm / MPa. Therefore, the performance of 5052 aluminum plate is significantly better than 3003 aluminum. 
From the commonly used specifications, 3003 aluminum plate to the main plate, plate application is not much; and 5052 aluminum plate in addition to thin plate, thick plate application is also very wide.
From the scope of application, 3003 aluminum plate is mainly used in wet environments, such as product packaging, refrigerators, air conditioning, cold storage, ventilation pipes and so on. The 5052 aluminum used in electrical appliances, traffic vehicles, pressure vessels, etc., is the manufacture of cars, aircraft fuel tanks, tubing commonly used materials. 3003 aluminum and 5052 aluminum plate, although often used as anti-rust aluminum, but the difference between the two kinds of aluminum is still very obvious, companies must be based on production needs to choose the right product.

5052 the main alloying elements are magnesium, with good forming processability, corrosion resistance, weldability, medium strength, used in the manufacture of aircraft fuel tanks, tubing, and traffic vehicles, ship's sheet metal parts, instruments, street lamps and rivets, Metal products, electrical appliances, and so on.
Based on the law of conservation of matter and the change of metal structure, the relationship between decarburization depth and size of 5052 aluminum plate before and after heat treatment was studied. A method for non-destructive testing of decarburization depth of 5052 aluminum plate was proposed. The experimental study was carried out and the experiment was carried out by 5052 aluminum plate heat treatment experiment.
Feedback
Contact Us
Tel: 15286802751
E-mail:ludi@mingtai-al.com
Address: Gongyi City,Henan Province,China
The latest price of aluminium plate for shipbuilding,automotive,aircraft and mold in malaysia aluminium plate manufacturer